EAA 3004乙烯丙烯酸共聚物
發布日期:2020-01-02     瀏覽量:935

PRIMACOR? 3004 Copolymer

陶氏塑料

產品說明

PRIMACOR? 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack

and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This

resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR).

? Excellent draw down and edge stability

? Excellent product resistance

? Excellent hot tack, heat seal, toughness

? High performance sealant or tie layer

Complies with:

? U.S. FDA 21 CFR 177.1310(b)

? EU, No 10/2011

Consult the regulations for complete details.

總體

材料狀態 ? 已商用:當前有效

供貨地區 ? 亞太地區

機構評級 ? EU No 10/2011 ? FDA 21 CFR 177.1310 (b)

形式 ? 顆粒料

物理性能 額定值 單位制 測試方法

比重 0.938 g/cm3 ASTM D792

ISO 1183

熔流率 2 (190°C/2.16 kg) 8.5 g/10 min ASTM D1238

ISO 1133

共聚單體含量 3 9.7 %

機械性能 額定值 單位制 測試方法

抗張強度 ASTM D638

ISO 527-2

屈服, 模壓成型 7.93 MPa

斷裂, 模壓成型 17.6 MPa

伸長率 (斷裂, 模壓成型) 600 % ASTM D638

ISO 527-2

熱性能 額定值 單位制 測試方法

維卡軟化溫度 81.1 °C ASTM D1525

ISO 306

溶融溫度(DSC 98.0 °C Internal Method

擠出 額定值 單位制 測試方法

熔體溫度 260 290 °C

內縮量 (288°C, 25.4 μm) 50.8 mm Internal Method

最小涂層厚度 10 μm Internal Method

最小涂層重量 9.8 g/m2 Internal Method

擠壓說明

擠出涂層薄膜的制造條件:

用于處理此樹脂的設備應由耐腐蝕材料制成。建議模具和適配器采用不銹鋼和/或雙面鍍鉻或鍍鎳。

? 螺桿尺寸:3.5 英寸 (89 mm);30:1 L/D

? 模具:30 英寸模具切邊至 24 英寸

? 模具間隙:20 密爾 (0.508 mm)

? 熔體溫度:550°F (288°C)

? 輸出:250 /小時

? 氣隙:6 英寸 (152 mm)

備注 1  一般屬性:這些不能被視為規格。

2  如同在生產時測量的一樣。 

返回列表
聯系我們
電話:0769-88768071 / 159-2060-9976 郭富民
座機:159-2060-9976
版權所有:東莞市友信新材料有限公司
地址:東莞市常平鎮大京九塑膠城塑通三路370-371號
備案號:粵ICP備18040684號
關注我們
在線咨詢
2019色?亚洲?日韩?国产 在线_高清无码一区二区在线观看_免费观看在线aⅴ天堂视频_久久亚洲?欧美 国产 综合